ALUSONG NANO coated aluminum composite panels are produced by a new and exciting NANO PAINT technology. A transparent NANO coat is applied over 2 or 3 PVDF coating to enhance the performance of the coated panels weatherability and durability resulting in longer color and glossy retention. The NANO coating prevents dirt, water, permanent spray paint, carbon monoxide, grease, oil or any foreign particles to penetrate through the paint surface. In addition, the NANO coating is a non-toxic, VOC EMISSION FREE coating system, which makes the surface self –cleaning and repellent to air-borne pollutants.
Aluminum alloy | AA1100 AA3003 AA5005 |
Aluminum skin | 0.21mm,0.30mm,0.35mm,0.40mm,0.45mm,0.5mm |
Panel thickness | 3mm,4mm,5mm,6mm |
Panel width | 1220mm,1250mm,1500mm |
Panel length | 2440mm,3050mm,4050mm |
Surface treatment | NANO PVDF |
Colors | 70 colors, RAL & PANTONE colors upon request |
Customers size | accepted |
GLOSSY | 30%-50% |
Panel width: ±2mm Panel length:±3mm
Panel thickness: ±0.2mm Panel diagonal: ≤5mm
Aluminum sheet thickness: ±0.01mm
Raw material:
Base material: high strength aluminum alloy sheet
PE core material: non-toxic low density polyethylene
Surface coating: NANO PVDF coating
Back coating: primer coating
Product properties
Excellent easy-cleaning
Pollution resistance
Oil resistance
Good friction resistance
Strong acid & alkali resistance
Outstanding weather resistance
1. Wall curtain, Cladding and Facade
2. Hotels and commercial mansions
3. Exterior renovation for old buildings
4. Subway and airports
5. Industry plants and materials,
6. Vehicle and boat materials
-
Application
-
Application
-
Application
-
Application
-
Application
-
Application
Description | Test standard | NANO PVDF |
Thickness of coating | PVDF paint≧34um | 35um to 37um |
Coating flexibility (T-bend) | Polyester paint≥2T | 2T |
Color different | ΔE≦2.0(follow color sample) | ΔE<2.0 |
Pencil hardness | ISO 15184:1998 Section 10 | 5H |
Chemical resistance | 5%HCI or 5% NaOH test in 24 hours -No change | No change |
Coating adhesion | ISO 15184:1998 Section 6 | The edges of the cut are completely smooth,none of the square of the lattice is detached. |
Resist solvent | No change for 200 times(MEK) | No change |
Boiling water resistance | EN438-2:2005 Section 12 | Rating 5,no visible change.Average change of mass: 0.08%;Average change of thickness:1.36% |
Peeling strength/stripping strength | BS EN319:1993 | 2.4N/mm2 |
Impact test for paint | ISO6272-1:2002 Section 8 | The coating not crack or peel after 2kg weight ball dropped from 1.5m height |
Abrasion resistance (L/Mil) | ISO7784-2:1997 Section 8 | The abrasive rubber wheel: Taber H-22; the cycles number:100; the mean loss mass:91mg |
Temperature resistance | EN438-2:2005 Section 19 | Rating 4, change of gloss only |
Coefficient of linear Thermal Expansion | ISO11359-2;1999 Section 7 | 1.3x10-4K |
Detergent resistance (3%) | ASTM D2248 | No change |
Humidity Resistance (3000hrs,100%RH,100°F) | ASTM D2247 | No change |
Salt spray resistance (3000hrs,5% salt) | ASTM B117 | No change |
Resistance to Staining | EN438-2:2005 Section 26 | Rating 5,no visible change |